It is a new generation, alcali free, highly effective liquid accelerating the hardening process for wet and dry shotcrete, , and providing higher resistance at final stages compared to conventional surface hardeners.
This product can be applied in the following areas:
Preparation of surface. The surface should be thoroughly removed of any kind of fat, rust, paraffin, and other residues preventing adhesion, and there should not be any residues remained on the surface. To save the adhesion, the surface should be cleaned with high-pressure water, and the product should be applied onto wet surface.
Selection of cement. To prevent negative effect during the period of hardening, fresh cement should be used. It is recommended to apply portland cement or sulfate-resistant cement to provide quick hardening of shotcrete.
Preparation of mixture. The water/cement ratio of shotcrete should be less than 0,45. This leads to the acceleration of hardening, obtaining of high initial and final strength, formation of thick layers on ceilings in more effective manner using smaller amounts of hardeners.
Application. During the application of wet system shotcrete, UnterMix 1162 is added to the concrete with a separate hose by means of pipe. During the application of dry system shotcrete, UnterMix 1162 is mixedwith water in a corresponding ratio before application. The mixture is added to the dry concrete mixture from a separate hose by means of spray gun.
The UnterMix 1162 product can be used in accordance with the following products:
Color: |
Transparent, brown |
Composition of product |
Aluminum hydroxide |
Density |
1,37 kg/liter |
Acidity (pH) |
2,5 |
Chlorine amount (EN 480-10) |
<0,1% |
Packing: |
10 kg cans, 200 kg casks, 1000 kg tanks, equipment with special tanks Special transport containers |
Consumption of the UnterMix 1162 product depends on concrete, surface and air temperature. Another important factor is compatibility with cement used. For this, prior tests should be done in order to define a corresponding consumption.
Depending on the application area, period of hardening, and resistance, the UnterMix 1162 product can be applied in the amount between 3-8% of the mass of mineral adhesive products (cement, volcanic ash, quartz sand, slag). In case the consumption exceeds the indicated limits, the final hardness limit may fall down.
The product should be stored at the temperature of more than +50C. In case of freezing, the product should be mixed with a mechanical mixer until it is totally homogeneous. The storage period is 3 months from the manufacturing date.