Cement based, acrylic emulsion polymer, high elasticity, enriched with chemical mixtures, two-component waterproofing mixture. Composition 1 is a grey color dry mixture, Composition 2 is an acrylic based emulsion polymer. The product conforms to the requirements of the TS AZS 31 43498-05-2005 specifications. For potable water reservoirs, resistant to ultraviolet radiation, extra waterproofing.

This insulating mixture can be applied in the following areas:

• indoor and outdoor areas;
• final layer of external wall surfaces;
• terraces;
• balconies;
• damp areas such as toilet rooms, bath-houses, kitchens, and others;
• swimming pools;
• water reservoirs suitable for potable water usage;
• in the sea water channels, applied in currentwise direction;
• in the areas where salt water dam is installed;
• protection of concrete surfaces from lime deposits and exposure to chlorine;
• waterproofing of planting areas.

• 1 mm layer of IzoLatexe UV provides degree of protection from lime deposits similar to concrete layer of more than 80 mm thickness;
• Waterproof and resistant to water pressure up to 4 bar;
• High adhesive force;
• Easy application and use;
• Long usage period;
• White color, resistant to ultraviolet radiation;
• High water vapor absorption capacity;
• Resistant to freezing and opening;
• High resistance to carbon dioxide and chlorine ions;
• While conventional waterproofing materials require a period of 7-28 days after laying concrete before application, IzoLatexe UV may be applied in 24 hours after concrete is laid;
• Suitable for application in potable water reservoirs.

Preparation of the surfaces. The cement based surfaces being in contact with water should be healthy, rigid, clean, dust-free, and should have suitable dimensions. The surface should be totally free of any fat, rust, paraffin, and other substances deteriorating adhesive force, and should not have small splinters. Small metal and wooden particles should be removed from the surface, cavities should be filled with Filkret repair mixture. Thoroughly soak the clean surface with water, then wait till it is half dry. Provide water saturation of the surface, otherwise it will quickly absorb the water contained in the product during application, and it will have matted appearance. So in case the work is performed at high ambient temperatures and windy conditions, the first layer of the product applied should include Component B with water content up to 10%.

Preparation of the mixture. Pour 8 kg of Component B liquid composite into clean mixing container, and gradually add 25 kg of Component A powder composite. Prepare the mixture for 3-5 minutes using 400-600 RPM mixer till the solution becomes entirely homogeneous. Mix again in approximately 3-5 minutes during 30-second period till the solution is entirely homogeneous.

Application. Spread the prepared IzoLatexe UV mixture over the surface in two or three layers using special brush. The brush movement directions should be perpendicular to each other. The time between applications of layers may be different, depending on the environmental conditions.

Recommendations. In case the temperature of the treated surface is below +50C and above +320C, the required temperature should be provided. The product should not be used in rainy or, windy weather conditions, or at excessive temperatures. The IzoLatexe UV waterproofing mixture applied at temperature of +230C achieves mechanical strength in 2 days, waterproofing features in 7 days, and final hardening in 14 days. In case the product is applied in the open air the treated surface should be protected from direct sun rays, wind, rain and frost during 24 hours. The cement and acrylic based systems are sensitive to the ambient and surface temperatures and humidity during application and reaction. Low temperatures reduce the reaction rate, and it results in elongation of the work execution period. High temperatures increase the reaction rate, and it results in decrease of the work execution period. To save the product water content and to achieve maximum effectiveness the temperature should not drop below the specified minimum value. The thickness of one wet layer should not exceed 2 mm. It is recommended to use “Matanat A” adhesives for the surface facing. After use all hand tools and devices should be cleaned with warm soapy water. After hardening the IzoLatexe UV product can be removed from the surface by mechanical means only.

The powder composite component can be stored during 12 months packed in original sacks in cold and dry conditions on wooden racks, maximum 10 sacks per rack, and the liquid component can be stored protected from freezing during 12 months in plastic cans placed one upon the other in three layers. In case the storage temperature is below 00C the composite component B may freeze.

• unpacked product should be used within one week;
• when using the product wear the appropriate protective clothing, safety gloves, glasses, and respirators;
• taking into consideration that it is a cement and acrylic based product containing chemical mixtures, immediately rinse it with large amount of water in case of contact with skin or eyes;
• do not add any substances not indicated in the application instructions;
• in case you swallow the product, immediately consult a physician;
• keep the product away from food products and children;
• parameters indicated above have been received on the basis of laboratory tests conducted in the ambient conditions of +230C±20C temperature and 50% + 5% humidity. Depending on the actual ambient conditions these parameters are subject to change.

• information indicated in technical specifications is based on scientific and experimental data;
• Matanat А company is responsible for the product quality only;
• with the exception of cases of works executed under the supervision of the company specialists, Мatanat  А company shall not be liable for any problems occuring due to improper use of the product by other persons;
• the company reserves the right to make changes in its product in consequence of scientific-and-technical development;
• for technical support and/or more information please do not hesitate to contact the Matanat А company!